LORD 606/6

Harmonization Code : 8529.90 | Parts solely or principally used for TV, radio, and transmission

LORD 606/6

Main features

  • Difficult Dcpd-Based FRP Bonding
  • 4 to 6-Minute Working Window
  • Glass-Bead Bondline Control

Product Description

LORD® 606 Acrylic Adhesive with LORD® Accelerator 6GB is a fast-setting, two-component structural acrylic adhesive system designed for bonding difficult composite substrates, including DCPD and modified DCPD resin-based fiber-reinforced plastics. The mixed adhesive can also cross-bond composites to supported metals and plastics while providing strong bonds, good surface cure and minimal surface preparation. Glass beads in LORD® Accelerator 6GB help control the adhesive bondline thickness.

Key Features

  • Composite bonding capability for DCPD-based FRP and cross-bonding composites to supported metals and plastics.
  • Fast room-temperature processing with a 4–6 minute working time and handling strength in 16–24 minutes at 75°F (24°C).
  • Controlled bondline thickness through the glass-bead content of LORD® Accelerator 6GB.
  • Non-sag application allows placement on vertical and overhead surfaces.

Applications / Suitable for

  • DCPD and modified DCPD resin-based FRP bonding
  • FRP-to-FRP structural bonding
  • Composite-to-metal cross-bonding
  • Composite-to-plastic cross-bonding
Product Family

LORD 606/6

Loading pricing…
TDS, SDS & Technical Documents

Technical Specifications

General Properties
Appearance
Appearance at room temperature.
White to Off-white Paste
Density
Volumetric mass per unit
1042 -1162 kg/m3
Physical Properties
Viscosity
Viscosity is a measurement of a fluid’s resistance to flow. Viscosity is commonly measured in centiPoise (cP). One cP is defined as the viscosity of water and all other viscosities are derived from this base. MPa is another common unit with a 1:1 conversion to cP. A product like honey would have a much higher viscosity -around 10,000 cPs- compared to water. As a result, honey would flow much slower out of a tipped glass than water would. The viscosity of a material can be decreased with an increase in temperature in order to better suit an application
100,000 - 300,000 mPa.s
Thermal Properties
Flash Point
The flashpoint of a solvent is the lowest possible temperature at which it can vaporize to form an ignitable vapor. Flashpoint is often confused with “autoignition temperature”, which is the temperature at which a solvent ignites without an ignition source.
15 °C

Additional Information

Technical Properties

As-Supplied / Before-Processing Properties

Typical properties of LORD® 606 Acrylic Adhesive and the mixed system with LORD® Accelerator 6GB. Values are typical and are not intended for specification purposes.

Property Value Unit Method / Condition
Appearance White to off-white paste — LORD 606 adhesive, typical
Viscosity 100,000–300,000 cP Typical
Density 8.7–9.7
(1042–1162)		 lb/gal
(kg/m³)		 LORD 606 adhesive, typical
Flash Point 59
(15)		 °F
(°C)		 Typical
Mix Ratio 7.3:1
10:1		 by weight
by volume		 LORD 606 adhesive to LORD Accelerator 6GB
Solids Content 100 % Mixed adhesive system
Working Time 4–6 minutes At 75°F (24°C)
Time to Handling Strength 16–24 minutes At 75°F (24°C); time to develop 100 psi
Mixed Appearance Grey paste — With LORD Accelerator 6GB
Shelf Life 6 months Store below 80°F (27°C) in the original, unopened container; 40–50°F (4–10°C) recommended
Technical Properties

After-Processing / Final-State Properties

Typical cured properties and supported bond-performance data for LORD® 606 Acrylic Adhesive with LORD® Accelerator 6GB. Values are typical and are not intended for specification purposes.

Property Value Unit Method / Condition
Complete Cure Time 8–24 hours Depends on temperature and bondline thickness
Cured Appearance White to grey — Tack-free surface
Elongation 12 % ASTM D882-83A, modified
Glass Transition Temperature (Tg) 225
(107)		 °F
(°C)		 ASTM E1640-99, by DMA
Aluminum-to-Aluminum Lap Shear 2776
(19.1)		 psi
(MPa)		 Room temperature; IPA-wiped aluminum; 0.010 in film; 24-hour room-temperature cure; 10:1 by volume
Galvanized-Steel Lap Shear 2063
(14.2)		 psi
(MPa)		 Room temperature; 0.010 in film; 24-hour room-temperature cure; 10:1 by volume
ABS-to-ABS Lap Shear 595
(4.1)		 psi
(MPa)		 Room temperature; 24-hour room-temperature cure; 10:1 by volume; stock-break failure
FRP-to-FRP Lap Shear 1106
(7.6)		 psi
(MPa)		 Room temperature; dry-rag-wiped FRP; 0.030 in film; 24-hour room-temperature cure; fiber-tear failure
FRP-to-ABS Lap Shear 440
(3.0)		 psi
(MPa)		 Room temperature; 24-hour room-temperature cure; stock-break failure